Accreditation by renowned testing institutions from Europe and UK, for Accelerated Weatherability Test (Artificial weathering up to 25000 hours), Mechanical properties & Chemical composition of our formulation.
| Properties | Standards | Range | Result | Accreditations From |
|---|---|---|---|---|
| Flexural Modulus of Elasticity | BS EN ISO 178:2013 | Not less than 2200 N/mm2 | 3070 N/mm2 | SK Z-Germany |
| Tensile Impact Strength | BS EN ISO 8256:2005 | Not less than 600 KJ/m2 | 934 KJ/m2 | SK Z-Germany |
| Accelerated Weathering [25000 Hours @ 50 GJ/m2] | DIN EN 513 | ΔE not more than 5 | 1.6 | SK Z-Germany |
| Charpy Impact Strength | BS EN ISO 179 -2:1999 | Not less than 20 KJ/m2 | 74.4 KJ/m2 | SK Z-Germany |
| Reduction in Charpy Impact Strength [Before & After Weathering] | DIN EN ISO 179 -1/1fA | Not More than 40% | 10.4 % | SK Z-Germany |
| Vicat Softening Temperature | BS EN ISO 306:1997 | Not less than 75oC | 80oC | SK Z-Germany |
| Heat Reversion @ 100o C, 60 Minutes | BS EN 12608-1:2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| Resistance to Impact of Main Profile by falling Mass @-10oC, | BS EN 12608-1:2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| Weld Strength (Individual Specimen) | BS EN 514:2000 | Not less than 20 Mpa | 25.32 Mpa | BSI-UK |
| Heat Aging @ 150oC,30 Minutes, | BS EN 12608-1;2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| RoHS | DIRECTIVE 2011/65/EU | Lead should not be detected | Not detected | SGS |
| Flammability | UL-94 | 10 Sec | Vo | CIPET |
| Limiting Oxygen Index (LOI) | ASTM D2863 | 45% | 47% | CIPET |
| Density | ASTM D 792 | Not More than 1.5 gm/cc | 1.46 gm/cc | CIPET |
| Thermal Conductivity | ASTM E-1530 | 0.12 to 0.25 W/mk | 0.137 W/mk | CIPET |
| Co-efficient of Linear Thermal Expansion | ASTM D 696 | Below 5x10-5 / oC | 3.82x10-5 / oC | CIPET |